PRODUCTS PTFE
OUTSTANDING PROPERTIES
EXCELLENT RESISTANCE TO CHEMICAL CORROSION
HIGH BREAKDOWN VOLTAGE / DIELECTRIC STRENGTH
BIOSAFE AND INERT
EXTREMELY LOW WATER AND GAS ABSORPTION
LOW STATIC AND DYNAMIC FRICTION COEFFICIENT
HIGHLY NON STICK FOR SMOOTH PASSAGE OF FLUIDS
HIGH TEMPERATURE RESISTANCE
DELIVERY PROGRAM, all dimensions in mm
PLAIN TUBING NATURAL & COLORED / STRIPED |
0.5 TO 25.0 ID X 0.75 TO 28.0 OD |
CORRUGATED TUBING NATURAL & BLACK |
6.0 ID TO 65.0 ID |
HEAT SHRINK TUBING NATURAL |
2.0 ID TO 100.0 ID |
TECHNICAL DATA SHEET
PROPERTY |
STANDARD |
VALUE |
|---|---|---|
Specific gravity |
ASTM D792 |
2.16 |
Tensile strength |
ASTM D638 |
24.5 Mpa |
Ultimate elongation |
ASTM D638 |
350 % |
Flexural modulus |
ASTM D790 |
490 Mpa |
Impact strength |
ASTM D256+23°C -54°C |
107 |
Hardness |
ASTM D2240 |
55 Shore D |
Coefficient of dynamic friction |
- |
0.1 |
Melting point |
- |
327 °C |
Service tempetature(20000h) with 50% retention of ultimate elongation |
- |
260 °C |
Inflammability |
UL-94 |
94 V-0 |
Dielectric constant at 103-106 Hz |
ASTM D150 |
2.1 |
Dielectric strength |
ASTM D150 |
24KV/mm |
Arc resistance |
ASTM D495(Stainless steel electrodes) |
>300 S |
Volume resistivity |
ASTM D257 |
>1018 Ωcm |
Weather resistance |
"Weather-O-meter"(2000h) |
- |
Solvent resistance |
ASTM D543 |
Excellent |
Chemical resistance |
ASTM D543 |
Excellent |
DISCLAIMER
- THE VALUES GIVEN IN THE DATA SHEET ARE FOR REFERENCE ONLY.
- CUSTOMERS ARE ADVISED TO TEST THE SUITABILITY OF OUR MATERIALS FOR THEIR APPLICATION AS THESE VALUES MAY NOT DIRECTLY HOLD GOOD UNDER ALL COMPLEX / MULTIPLE APPLICATION CONDITIONS.
- OUR COMPANY DOES NOT UNDERTAKE ANY LIABILITY, DIRECT OR INDIRECT, LINKED WITH THE USAGE AND PERFORMANCE OF OUR MATERIALS UNDER APPLICATION CONDITIONS.
- CUSTOMERS ARE ADVISED TO TEST THE SUITABILITY OF OUR MATERIALS FOR THEIR APPLICATION AS THESE VALUES MAY NOT DIRECTLY HOLD GOOD UNDER ALL COMPLEX / MULTIPLE APPLICATION CONDITIONS.
- OUR COMPANY DOES NOT UNDERTAKE ANY LIABILITY, DIRECT OR INDIRECT, LINKED WITH THE USAGE AND PERFORMANCE OF OUR MATERIALS UNDER APPLICATION CONDITIONS.