PRODUCTS FEP
OUTSTANDING PROPERTIES
EXCELLENT RESISTANCE TO CHEMICAL CORROSION
HIGH BREAKDOWN VOLTAGE / DIELECTRIC STRENGTH
BIOSAFE AND INERT
LOW WATER AND GAS ABSORPTION
TRANSPARENT TO LIGHT AND RAYS
NON STICK FOR SMOOTH PASSAGE OF FLUIDS
HIGH TEMPERATURE RESISTANCE UPTO 200 DEG C
DELIVERY PROGRAM, all dimensions in mm
PLAIN TUBING NATURAL & COLORED / STRIPED |
1.0 TO 35.0 ID X 2.0 TO 38.0 OD |
CORRUGATED TUBING NATURAL & BLACK |
6.0 ID TO 65.0 ID |
HEAT SHRINK TUBING NATURAL & COLORED |
2.0 ID TO 100.0 ID ON REQUEST |
TECHNICAL DATA SHEET
PROPERTY |
STANDARD |
VALUE |
|---|---|---|
Specific gravity |
ASTM D792 |
2.15 |
Tensile strength |
ASTM D638 |
31 Mpa |
Ultimate elongation |
ASTM D638 |
305 % |
Flexural modulus |
ASTM D790 |
586 Mpa |
Impact strength |
ASTM D256+23°C -54°C |
155 |
Hardness |
ASTM D2240 |
57 Shore D |
Coefficient of dynamic friction |
- |
0.2 |
Melting point |
- |
260 °C |
Service tempetature(20000h) with 50% retention of ultimate elongation |
- |
205 °C |
Inflammability |
UL-94 |
94 V-0 |
Dielectric constant at 103-106 Hz |
ASTM D150 |
2.1 |
Dielectric strength |
ASTM D150 |
45KV/mm |
Arc resistance |
ASTM D495(Stainless steel electrodes) |
>300 S |
Volume resistivity |
ASTM D257 |
>1018 Ωcm |
Weather resistance |
"Weather-O-meter"(2000h) |
- |
Solvent resistance |
ASTM D543 |
Excellent |
Chemical resistance |
ASTM D543 |
Excellent |
DISCLAIMER
- THE VALUES GIVEN IN THE DATA SHEET ARE FOR REFERENCE ONLY.
- CUSTOMERS ARE ADVISED TO TEST THE SUITABILITY OF OUR MATERIALS FOR THEIR APPLICATION AS THESE VALUES MAY NOT DIRECTLY HOLD GOOD UNDER ALL COMPLEX / MULTIPLE APPLICATION CONDITIONS.
- OUR COMPANY DOES NOT UNDERTAKE ANY LIABILITY, DIRECT OR INDIRECT, LINKED WITH THE USAGE AND PERFORMANCE OF OUR MATERIALS UNDER APPLICATION CONDITIONS.
- CUSTOMERS ARE ADVISED TO TEST THE SUITABILITY OF OUR MATERIALS FOR THEIR APPLICATION AS THESE VALUES MAY NOT DIRECTLY HOLD GOOD UNDER ALL COMPLEX / MULTIPLE APPLICATION CONDITIONS.
- OUR COMPANY DOES NOT UNDERTAKE ANY LIABILITY, DIRECT OR INDIRECT, LINKED WITH THE USAGE AND PERFORMANCE OF OUR MATERIALS UNDER APPLICATION CONDITIONS.